Precision of polyether ether ketone (PEEK) or cobalt-chrome implant bar fit to implants after mechanical cycling / Precisão da adaptação de barras tipo protocolo confeccionados em polyetheretherketone (PEEK) ou cobalto cromo sobre implante após ciclagem mecânica

ABSTRACT Based on its mechanical properties, PEEK (polyether-ether-ketone) might be useful in restorative procedures. In oral rehabilitation, its viability has been studied mainly for prostheses and dental implants. Aim: The aim of this study was to evaluate the fit accuracy of dental implant bars made of either PEEK or cobalt-chrome submitted to cycling mechanics. Materials and Method: This was an experimental in vitro study, where units were treated with two implants and mini-abutments, joined by cobalt-chrome or polyether-ether-ketone PEEK bars. A total 20 bars were prepared (n=10 per group) and subjected to mechanical cycling tests (1 million cycles on the distal cantilever of the bar in the vertical direction, 120N and sinusoidal loading, at a frequency of 2Hz). The fit at the abutment/implant interface was measured before and after cycling, and the counter-torque of the vertical screw of the mini abutments was measured after cycling, using a digital torquemeter. Data were analyzed by three-way ANOVA and Tukey's test at 5% significance level. Results: No statistically significant interaction was found among the three factors considered (bar material, implant positioning and mechanical cycling) (p = 0.592). No significant difference was identified in the interaction between bar material and implant positioning (p = 0.321), or between implant positioning and mechanical cycling (p = 0.503). The association between bar material and mechanical cycling was statistically significant (p = 0.007), with the cobalt-chrome bar resulting in greater misfit with mechanical cycling. There was no difference in counter-torque values between groups. Conclusions: The PEEK bar provided better fit of the mini abutments to the implants, even after mechanical cycling. The counter-torque of the screws was similar in all scenarios considered.

RESUMO O PEEK (Poli-éter-éter-cetona) é um material considerado para uso em procedimentos restauradores devido às suas propriedades mecânicas. Na reabilitação oral, sua viabilidade tem sido estudada principalmente para uso em próteses e implantes dentários. Objetivos: O objetivo deste estudo foi avaliar a precisão da adaptação de duas barras diferentes do tipo protocolo confeccionadas em PEEK ou Cobalto-Cromo, após serem submetidas à mecânica ciclística. Materiais e Método: As unidades experimentais foram constituídas por barras confeccionadas em Poli-ether-ether-Ketone (PEEK) e em Cobalto-Cromo (Co-Cr). Trata-se de um estudo experimental, in vitro, onde verificou-se unidades constituídas por dois implantes e mini pilares unidos com barras de Cobalto-Cromo ou PEEK. Foram confeccionados um total de 20 barras (n=10 em cada grupo) e as barras foram submetidas a ensaios de ciclagem mecânica (1 milhão de ciclos no cantilever distal da barra no sentido vertical, 120N e carregamento senoidal, a uma frequência de 2Hz). Antes e após a ciclagem realizou-se a mensuração da desadaptação na interface pilar/implante e após a ciclagem foi medido o contra-torque do parafuso vertical dos mini-pilares através de torquímetro digital TQ 8800 (LT Lutron, Taiwan). Os dados foram submetidos a ANOVA a três critérios e teste de Tukey ao nível de significância a 5%. Resultados: Constatou-se que não houve interação estatisticamente significativa entre os três fatores estudados, ou seja, entre o material da barra, o posicionamento do implante e a ciclagem mecânica (p = 0,592). Também não se identificou diferença estatística significativa da interação entre o material da barra e o posicionamento do implante (p = 0,321), nem entre o posicionamento do implante e a ciclagem mecânica (p = 0,503). Já a associação entre o material da barra e a ciclagem mecânica foi estatisticamente significativa (p = 0,007), onde a barra de Cobalto-Cromo resultou em maior desadaptação com a ciclagem mecânica. Não houve diferença nos valores dos contra-torques entre os grupos. Conclusões: Conclui-se que a barra de protocolo fabricada em PEEK proporcionou melhor adaptação dos mini pilares aos implantes mesmo após a ciclagem mecânica. Por fim, o contra-torque dos parafusos foi semelhante em todos os cenários avaliados.

Ozone gas therapy for tooth bleaching preserves enamel microhardness, roughness and surface micromorphology / Ozonioterapia gasosa para clareamento dental preserva a microdureza, rugosidade e micromorfologia superficial do esmalte

ABSTRACT After ozone therapy for bleaching, it is important to evalúate enamel surface properties, to ensure that bleaching provides adequate conditions for sound dental substrate. Aim: The aim of this in vitro study was to evaluate the effects of a bleaching treatment with 10% carbamide peroxide (CP), with or without ozone (O), on the microhardness, roughness and micromorphology of the enamel surface. Materials and Method: Bovine enamel blocks were planed and distributed among the following three bleaching treatment groups (n=10): CP - 1 hour per day/14 days (Opalescence PF 10%/ Ultradent); O - 1 hour per day every 3 days/3 sessions (Medplus VPhilozon, 60 mcg/mL and oxygen flow rate of 1 L/min); and OCP - CP with O, 1 hour per day every 3 days/3 sessions. Enamel surface microhardness (Knoop), roughness (Ra), and micromorphology by scanning electron microscopy (5,000x magnificaron) were determined before and after the treatments. Results: ANOVA and Tukey-Kramer's test showed that enamel microhardness remained unchanged by treatment with O and OCP (p=0.0087), but decreased by treatment with CP. Treatment with O promoted higher enamel microhardness than the other groups (p=0.0169). Generalized linear mixed models for repeated measures over time indicated treatment with CP increased enamel roughness more than OCP or O (p=0.0003). CP produced slight irregularities in enamel micromorphology after the whitening treatment. O, with or without CP, maintained the mechanical and physical properties of microhardness and enamel surface micromorphology, and either maintained or reduced surface roughness, compared to the conventional tray-delivered CP bleaching treatment. Conclusions: Treatment with 10% carbamide peroxide in trays promoted greater changes in enamel surface properties than treatments with ozone and with 10% ozonized carbamide peroxide in the office.

RESUMO É importante avaliar as propriedades da superficie do esmalte após a aplicagao da ozonioterapia para clareamento, para garantir que o efeito clareadorproporcione condigoes adequadaspara um substrato dentário higido. Objetivo: O objetivo deste estudo in vitro foi avaliar os efeitos de um tratamento clareador com peróxido de carbamida (PC) a 10%, associado ou nao ao ozonio (O), na microdureza, rugosidade e micromorfologia da superficie do esmalte. Materials e Método: Blocos de esmalte bovino foram aplainados e distribuidos entre tres grupos de tratamento clareador (n=10): PC - 1 hora por dia/14 dias (Opalescence PF 10%/ Ultradent); O - 1 hora por dia a cada 3 dias/3 sessoes (Medplus VPhilozon, 60 mcg/mL e fluxo de oxigenio de 1 L/min); e PCO - CP com O, 1 hora por dia a cada 3 dias/3 sessoes. A microdureza (Knoop), a rugosidade (Ra) e a micromorfologia da superficie do esmalte avaliada por microscopia eletronica de varredura (aumento de 5.000x) foram analisadas antes e após os tratamentos. Resultados: ANOVA e teste de Tukey-Kramer mostraram que O e PCO mantiveram os valores de microdureza do esmalte ao final do tratamento (p=0,0087), enquanto PC promoveu diminuigao da microdureza. O promoveu maiores valores de microdureza do esmalte do que os outros grupos ao final do tratamento (p=0,0169). Modelos lineares generalizados mistos para medidas repetidas no tempo indicaram um aumento na rugosidade da superficie para PC, levando a maior rugosidade do esmalte ao final do tratamento, em comparagao com PCO ou O (p=0,0003). PC apresentou pequenas irregularidades na micromorfologia do esmalte após o tratamento clareador. O, com ou sem PC, manteve as propriedades mecánicas e fisicas de microdureza e micromorfologia da superficie do esmalte, e manteve ou reduziu a rugosidade da superficie, em comparagao com o tratamento clareador a base de PC aplicado em moldeira convencional. Conclusoes: O tratamento com peróxido de carbamida a 10% para uso em moldeiras promoveu maiores alteragoes nas propriedades de superficie do esmalte do que aquelas observadas nos tratamentos com ozonio e com peróxido de carbamida ozonizado a 10% para uso em consultório.

The potential of salivary albumin to degrade composite resin / Albumina salivar: investigando seu potencial de degradar resinas compostas

ABSTRACT Albumin is a salivary enzyme capable of cleaving ester linkages and catalyzing degradation of resin-based dental materials. However, the effect of concentration-dependent esterolytic action on composite resins as yet remains unexplored. Aim: The purpose of this study was to evaluate whether artificial saliva formulations with different concentrations of albumin affected the surface roughness, flexural strength and microhardness of a composite resin. Materials and Method: Specimens (25x2x2mm) of a nanofilled composite (Filtek Z350XT, 3M/ESPE) were prepared and analyzed for average surface roughness (Ra/pm). The specimens were then allocated to 6 groups (n=30), to be treated with different salivary albumin concentrations: 0, 10, 50, 100, 200, 400 pg/mL. The specimens were stored in their respective artificial saliva groups, half of them for 24 h and the remainder for 180 days (artificial saliva renewed weekly), after which they were submitted to a new Ra reading, and tested for three-point flexural strength (FS, MPa). The specimens stored for 180 days were analyzed for Knoop microhardness (KH, Kg/mm2). Data were submitted to two-way ANOVA (Ra and FS) and one-way ANOVA (KH). Results: Although Ra increased (p < 0.001) and FS decreased (p < 0.001) from 24 hours to 180 days of storage, the albumin concentration did not significantly affectRa (p = 0.168), FS (p = 0.477) or KH (p = 0.378). Conclusion: The esterolytic action of albumin did not increase the artificial-saliva-induced hydrolytic degradation of the composite resin.

RESUMO Albumina, uma enzima encontrada na saliva, é capaz de clivar ligagoes éster e catalisar a degradando de materiais dentários á base resina. Apesar da agao esterolítica ser potencialmente concentragao-dependente, a investigando desse efeito sobre resinas compostas ainda permanence inexplorado. Objetivo: O objetivo deste estudo foi avaliar se formulagoes de saliva artificial contendo diferentes concentragoes de albumina afetariam a rugosidade superficial, a resistencia flexural e a microdureza de uma resina composta. Materials e Método: Corpos de pro-va em barra (25x2x2mm) foram confeccionados a partir de uma resina composta nanoparticulada (Filtek Z350XT, 3M/ESPE) e foram submetidos á leitura de rugosidade superficial média inicial (Ra, pm), em rugosímetro. Entao, as amostras foram divididas em 6 grupos (n=30) de acordo com a concentrando de albumina na saliva: 0, 10, 50, 100, 200, 400 pg/mL. As amostras foram armazenadas nas formulagoes de saliva artificial correspondente ao seu grupo, metade por 24 h e as demais por 180 dias (com trocas de saliva semanais). As amostras foram submetidas a no-vas leituras de rugosidade (Rafinal) e avaliadas quanto á resistencia flexural de tres pontos (RF, MPa). As amostras armazenadas por 180 dias foram avaliadas quanto á microdureza Knoop (KH, Kg/mm2). Os dados foram submetidos a análises de variáncia a dois critérios (Ra e RF) e a um critério (KH). Resultados: Apesar de haver aumento na Ra (p < 0,001) e uma diminuigao da RF (p < 0,001) de 24 h para 180 dias, a concentragao de albumina nao afetou significativamente a Ra (p = 0,168), a RF (p = 0,477) ou a KH (p = 0,378). Conclusoes: A agdo esterolítica da albumina nao aumentou a degradagao hidrolítica da resina composta induzida pela saliva artificial.

Bonding strategy of a universal adhesive system containing chitosan: influence on dentin permeability, and effect on adhesive layer micromorphology / Estratégia de união de um sistema adesivo universal contendo quitosana: influência na permeabilidade dentinária e efeito na micromorfologia da camada do adesivo

ABSTRACT Aim: This study evaluated the influence of chitosan added to a universal adhesive system used in totaletch (TE) or self-etch (SE) mode on dentin permeability, and on the micromorphology of the adhesive layer. Materials and Method: Dentin discs were obtained from human third molars and randomly distributed according to bonding strategy (TE or SE), and to whether or not 1% chitosan (C) was added to a universal adhesive system (Single Bond Universal/3M ESPE), to create the following groups (n=10): TE, TEC, SE, and SEC. Dentin permeability was measured at baseline and after application of dentin treatments. The surface of the adhesive layer (AL) and the dentin adjacent to the AL were examined under a scanning electron microscope. Results: There were no significant differences in permeability percentage between the groups with and without C (TE and SE versus TEC and SEC) (p>0.05; Mann Whitney test). Dentin permeability was lower when the adhesive system was applied in the SE mode, regardless of the addition of C. The micromorphology of the AL surface showed irregularities, and a greater degree of porosity, when the adhesive system was applied in the SE mode, regardless of chitosan addition. There was a greater depth of penetration of the adhesives into the dentin adjacent to the AL in both the TE and TEC groups. Chitosan added to the adhesive system did not influence dentin permeability. Conclusions: The self-etch strategy led to lower dentin permeability, and to more irregularities on the surface of the adhesive layer.

RESUMO Objetivo: Este estudo avaliou a influência da quitosana adicionada a um sistema adesivo universal usado no modo total-etch (TE) ou self-etch (SE) na permeabilidade dentinária e na micromorfologia da camada adesiva. Materiais e método: Discos de dentina foram obtidos de terceiros molares humanos e distribuídos aleatoriamente de acordo com a estratégia de união (TE ou SE), e para incorporação ou não de quitosana a 1% (Q) em um sistema adesivo universal (Single Bond Universal/3M ESPE), para obter os seguintes grupos (n=10): TE, TEQ, SE e SEQ. A permeabilidade da dentina foi medida no início e após a aplicação dos tratamentos de dentina. A superfície da camada adesiva (CA) e a dentina adjacente à CA foram examinadas em microscópio eletrônico de varredura. Resultados: Não houve diferenças significativas no percentual de permeabilidade entre os grupos com e sem Q (TE e SE versus TEQ e SEQ) (p>0,05; teste de Mann Whitney). Houve um menor percentual de permeabilidade dentinária quando o sistema adesivo foi aplicado no modo SE, independentemente da incorporação de Q. A micromorfologia da superfície da CA apresentou irregularidades e maior grau de porosidade quando o sistema adesivo foi aplicado no modo SE, independentemente da adição de Q. Houve maior profundidade de penetração dos adesivos na dentina adjacente à CA nos grupos TE e TEQ. A quitosana adicionada ao sistema adesivo não influenciou a permeabilidade dentinária. Conclusões: A estratégia autocondicionante levo

Bulk-fill restorative composites under simulated carious and erosive conditions / Resinas compostas restauradoras bulk-fill sob condiçöes simuladas de cárie e erosão

ABSTRACT Acidic conditions can cause hydrolysis and accelerate degradation of resin composites (RCs). Since there are limited and controversial data on the effect of acids on bulk-fill RCs, this study assessed the surface roughness (SR) and flexural strength (FS) of these RCs under simulated carious and erosion conditions. Bars of Filtek Bulk Fill (FBF, 3M/ESPE), X-tra fil (XTF, Voco), Tetric N-Ceram Bulk Fill (TBF, Ivoclar/Vivadent), and Aura Bulk Fill (ABF, SDI) and a conventional RC [Filtek Z350XT (FZ, 3M/ESPE)] were allocated (n=15) to undergo caries or erosion conditions. The control group was kept in artificial saliva (AS). The bars were evaluated for SR change (final-baseline) and for three-point FS. Data were analyzed using ANOVA and Tukey's test. At the baseline (p <0.001), the SR of RCs ranked as follows: (TBF = XTF) < FBF (none differed from FZ) < ABF. The interplay between RCs and conditions affected SR change (p = 0.025). While after storage in AS, there was no difference among RCs, following carious and erosive conditions, ABF showed higher SR change. For FS (p <0.001), XTF > (FBF = FZ) > (TBF = FZ) > ABF, with no difference among control, carious and erosive conditions (p = 0.148). Depending on the restorative bulk-fill RCs, carious and erosive conditions roughen the surface but do not affect the FS of these materials.

RESUMO Condições acídicas podem causar hidrólise e acelerar a degradação de resinas compostas (RCs). Como há dados limitados e controversos sobre os efeitos de ácidos sobre RCs bulk-fill, este estudo avaliou a rugosidade de superfície (RS) e a resistência flexural (RF) dessas RCs sob condições simuladas de cárie e erosão. Barras de Filtek Bulk Fill (FBF, 3M/ESPE), X-tra fil (XTF, Voco), Tetric N-Ceram Bulk Fill (TBF, Ivoclar/Vivadent) e Aura Bulk Fill (ABF, SDI) e de uma RC convencional [Filtek Z350XT (FZ, 3M/ESPE)] foram alocadas (n=15) para estarem sob condições cariogênicas ou erosivas. O grupo controle foi mantido em saliva artificial saliva (SA). As barras foram avaliadas quanto à alteração de RS (final-inicial) e à RF de três pontos. Os dados foram analisados utilizando ANOVA e teste de Tukey. Inicialmente (p <0,001) a RS das RCs foi a seguinte: (TBF = XTF) < FBF (nenhuma diferiu de FZ)< ABF. A interação entre as RCs e as condições acídicas influenciou a alteração de RS (p = 0,025). Após armazenamento na SA, não houve diferença entre as RCs, enquanto após condições cariogênicas e erosivas a ABF mostrou a maior alteração de RS. Para FS (p < 0,001), XTF > (FBF = FZ) > (TBF = FZ) >ABF, sem diferença entre controle e condições cariogênicas e erosivas (p = 0,148). Dependendo da RC bulk-fill restauradora, condições cariogênicas e erosivas aumentam a RS, mas não alteram a RF desses materiais.

Influence of fluoride-releasing materials in the inhibition of enamel and dentin demineralization around restorations / Influência de materiais liberadores de flúor na inibição da desmineralização do esmalte e da dentina ao redor de restaurações

Objective: The aim was to evaluate the influence of fluoride-releasing restorative materials in enamel and dentin microhardness. Material and Methods: 40 blocks (5x5x3 mm) from cervical third of human molars received a cavity preparation between the enamel and dentin, and the restorations were subjected to in vitro caries model. Specimens were randomly restored with (n=10): conventional glass ionomer cement (Ketac Cem, 3M ESPE); polyacid-modified composite resin (Ionoseal, VOCO); resin-modified glass ionomer cement (Ionofast, Biodinâmica); or microhybrid composite resin (Filtek Z250, 3M ESPE). The specimens were sectioned longitudinally and enamel and dentin Knoop microhardness were determined at different distances from the restorative material (100, 200 and 300 µm) and depth of surface (20, 40 and 60 µm). The data were submitted to three-way repeated measures ANOVA and Tukey ́s test ( α =0.05). Results: For enamel, the double interactions between material x distance and material x depth were statistically significant. In all depths and distances, the highest values of enamel microhardness were observed for Ketac Cem. In dentin, the materials differed statistically from each other, and Ionoseal obtained higher microhardness values than those found in Ionofast. Conclusion: Conventional glass ionomer cement is more effective in preventing enamel demineralization around restoration followed by the polyacid-modified composite resin. In dentin, the polyacid-modified composite resin obtained better performance than resin-modified glass ionomer cement. (AU)

Objetivo: O objetivo foi avaliar a influência de materiais restauradores liberadores de flúor na microdureza do esmalte e da dentina. Material e Métodos: 40 blocos (5x5x3 mm) do terço cervical de molares humanos receberam preparo cavitário entre esmalte e dentina, e após a restauração foram submetidas a um modelo in vitro de cárie. As amostras foram restauradas aleatoriamente com (n=10): cimento de ionômero de vidro convencional (Ketac Cem, 3M ESPE); resina composta modificada por poliácidos (Ionoseal, VOCO); cimento de ionômero de vidro modificado por resina (Ionofast, Biodinâmica); ou resina composta microhíbrida (Filtek Z250, 3M ESPE). As amostras foram seccionadas longitudinalmente e a microdureza Knoop de esmalte e dentina foi determinada em diferentes distâncias do material restaurador (100, 200 e 300 µm) e profundidade de superfície (20, 40 e 60 µm). Os dados foram submetidos à ANOVA para medidas repetidas de três fatores e teste de Tukey (α =0,05). Resultados: Para o esmalte, as duplas interações entre material x distância e material x profundidade foram estatisticamente significativas. Em todas as profundidades e distâncias, os maiores valores de microdureza do esmalte foram observados para o Ketac Cem. Na dentina, Ionoseal obteve valores de microdureza superiores aos encontrados no Ionofast. Conclusão:O cimento de ionômero de vidro convencional é mais eficaz na prevenção da desmineralização do esmalte ao redor da restauração, seguido pela resina composta modificada por poliácidos. Na dentina, a resina composta modificada por poliácidos obteve melhor desempenho que o cimento de ionômero de vidro modificado por resina. (AU)

Low- and high-viscosity bulk-fill resin composites / Resinas compostas bulk-fill de baixa e alta viscosidade

ABSTRACT The aim of this study was to compare low- and high-viscosity bulk-fill composites for Knoop microhardness (KHN), microtensile bond strength (MTBS) to dentin in occlusal cavities, and fracture strength (FS) in molars with mesialocclusal- distal restoration. Disk-shaped samples with different thicknesses (2 or 4 mm) of low-viscosity (SDR Flow, Dentsply) and high-viscosity bulk-fill composites (Filtek BulkFill, 3M ESPE; and Tetric-N Ceram Bulk Fill, Ivoclar Vivadent) were prepared for top and bottom KHN analysis (n=10). MTBS to dentin and fracture pattern was evaluated in human molars with occlusal cavities restored with (n=10): conventional nanocomposite (Z350XT, 3M ESPE), low-viscosity (Filtek Bulk-fill Flow, 3M ESPE) or high-viscosity bulk-fill composites (Filtek BulkFill). The FS and fracture pattern of human molar with mesial-occlusal-distal restorations submitted or not to thermomechanical cycling were investigated (n=10) using: intact tooth (control), and restoration based on conventional microhybrid composite (Z250, 3M ESPE), low-viscosity (SDR Flow) or high-viscosity bulk-fill composites (Filtek BulkFill). The data were submitted to split-plot ANOVA (KHN), one-way ANOVA (MTBS), two-way ANOVA (FS) followed by Tukey's test (α=0.05). For KHN, there was no significant difference for the resin composites between the top and bottom. For MTBS, no significant differences among the materials were detected; however, the low-viscosity composite presented lower frequency of adhesive failures. For FS, there was no significant difference between composites and intact tooth regardless of thermomechanical cycling. Low- and high-viscosity bulk-fill composites have comparable microhardness and microtensile bond strength when used in occlusal restorations. Likewise, the bulk-fill composites present similar fracture strength in molars with mesio-occlusal-distal restorations.

RESUMO O objetivo deste estudo foi comparar resinas compostas bulk- -fill de baixa e alta viscosidade quanto à microdureza Knoop (KHN), resistência de união a microtração (MTBS) em cavidades oclusais e carga à fratura (FS) em molares com restauração mesio-oclusal-distal. Amostras em forma de disco com diferentes espessuras (2 ou 4 mm) de resinas bulk-fill de baixa viscosidade (SDR Flow, Dentsply) e alta viscosidade (Filtek BulkFill, 3M ESPE; e Tetric-N Ceram Bulk Fill, Ivoclar Vivadent) foram obtidas para análise de KHN no topo e na base (n = 10). A MTBS em dentina e o padrão de fratura foram avaliados em molares humanos com cavidades oclusais restauradas com (n = 10): resina composta nanoparticulada convencional (Z350XT, 3M ESPE), resinas bulk-fill de baixa viscosidade (Filtek Bulk-fill Flow, 3M ESPE) ou alta viscosidade (Filtek BulkFill). Foram investigados a FS e o padrão de fratura de molares humanos em restaurações mesial-ocluso-distais sub metidas ou não à ciclagem termomecânica (n = 10), sendo: dente íntegro (controle), e restaurações baseadas em resina composta microhíbrida convencional (Z250, 3M ESPE); resinas bulk-fill de baixa viscosidade (SDR Flow) ou alta viscosidade (Filtek BulkFill). Os dados foram submetidos a split-plot ANOVA (KHN), one-way ANOVA (MTBS), two-way ANOVA (FS) seguidos do teste de Tukey (α = 0,05). Para KHN, não houve diferença significativa entre o topo e a base para as resinas compostas. Para MTBS, não foram detectadas diferenças significativas entre os materiais; entretanto, a resina bulk-fill de baixa viscosidade apresentou menor frequência de falhas adesivas. Para FS, não houve diferença significativa entre os materiais e o dente íntegro, independentemente da ciclagem termomecânica. As resinas bulk-fill de baixa e alta viscosidade têm microdureza e resistência à microtração comparáveis quando usados em restaurações oclusais. Da mesma forma, as resinas bulk-fill apresentam resistência à fratura semelhante em molares com restaurações mesio-oclusal-distais.

Effect of bleaching protocols on surface roughness and color change of high- and low-viscosity bulk-fill composite resins / Efeito de protocolos clareadores na rugosidade de superfície e alteração de cor de resinas compostas bulk-fill de alta e baixa viscosidade

ABSTRACT The aim of this in vitro study was to evaluate the effect of bleaching protocols on the surface roughness (Ra), color change and surface micromorphology of a low-viscosity bulk-fill composite (Filtek Bulk Fill Flow, 3M ESPE), a highviscosity bulk-fill composite (Filtek Bulk Fill, 3M ESPE) and a conventional nanoparticulate composite resin (control) (Filtek Z350 XT, 3M ESPE). Forty samples of each composite (disks 5 mm in diameter and 2 mm thick) were randomly divided into four groups (n=10), according to bleaching protocol: a) 10% carbamide peroxide gel (Opalescence, Ultradent Products) (2 h/ day, for 14 days); b) 40% hydrogen peroxide gel (Opalescence Boost, Ultradent Products) (three bleaching sessions, once a week, 45 min/session); c) whitening rinse (Listerine Whitening Extreme, Johnson & Johnson) (2 min/day, for 14 days); and d) distilled water (control). The samples were submitted to triplicate readings (Ra and color [CIELAB parameters]) before and after contact with bleaching protocols. Micromorphology was analyzed in a scanning electron microscope (SEM). Ra and color parameters (ΔL, Δa, Δb and ΔE) were analyzed by generalized linear models (α=0.05). The Ra of the high-viscosity bulk-fill was significantly higher than that of the other composites (p<0.05). Ra increased significantly (p<0.05) and surface became more irregular (SEM analysis) in all the composite resins, regardless of the bleaching protocol (p<0.05). The high-viscosity bulk-fill composite resin group had significantly lower ΔE (p<0.05) than the nanoparticulate composite resin group immersed in distilled water. It was concluded that the characteristics of each resin significantly influenced the Ra more than the bleaching protocol. The high-viscosity bulk-fill resin presented minor color change.

RESUMO Este estudo in vitro teve objetivo de avaliar o efeito de protocolos clareadores sobre a rugosidade de superfície (Ra), alteração de cor e micromorfologia de resina bulk-fill de baixa viscosidade (Filtek Bulk Fill Flow, 3M ESPE), alta viscosidade (Filtek Bulk Fill, 3M ESPE) e de uma resina composta nanoparticulada (controle) (Filtek Z350 XT, 3M ESPE). Quarenta amostras de cada resin composta (discos de 5 mm de diâmetro e 2 mm de espessura) foram aleatoriamente divididas em quatro grupos , de acordo com protocolo clareador (n=10): a) Gel de peróxido de carbamida (Opalescence, Ultradent Products) (2 horas/dia, por 14 dias); b) Gel de peróxido de hidrogênio (Opalescence Boost, Ultradent Products) (3 sessões de clareamento, uma por semana, 45 min/sessão); enxaguatório clareador (Listerine Whitening Extreme, Johnson & Johnson) (2 min/dia, por 14 dias); d) água destilada (controle). As amostras foram submetidas a leituras, em triplicata (Ra e cor (parâmetros CIELab) antes e depois do contato com os protocolos clareadores. A micromorfologia de superfície foi conduzida em microscópio eletrônico de varredura (MEV). Ra e parâmetros de cor (ΔL, Δa, Δb e ΔE) foram analisados por modelos lineares generalizados (α=0.05). A Ra da resina bulk-fill de alta viscosidade foi significantemente superior do que para os outros compósitos (pp<0.05). A Ra aumentou significantemente (p<0.05) e a superfície ficou mais irregular (MEV) para todos os compósitos, independente do protocolo clareador (pp<0,05). A resina bulk-fill de alta viscosidade obteve menor ΔE (pp<0.05) do que a resina composta nanoparticulada, imersa em água destilada. Pode-se concluir que as características de cada resina composta influenciaram de forma mais significativa a Ra do que o protocolo clareador. A resina bulk fill de alta viscosidade apresentou menor alteração de cor.

Oval versus circular-shaped root canals: bond strength reached with varying post techniques

Abstract The aim of this study was to compare the bond strength (BS) of glass fiber posts (GFP) luted to oval and circular-shaped root canals rehabilitated using varying post techniques, at different intraradicular levels. Ninety 16-mm-long roots of human mandibular premolars, classified either as having oval or circular-shaped canals, were endodontically treated and prepared for restoration using one of three different post techniques (n=15): 1) single GFP; 2) resin-relined GFP; 3) main GFP associated with accessory posts. GFPs were luted with a dual polymerizing resin cement (RelyX ARC) after the canal had been treated with a 3-step etch-and-rinse adhesive system (Adper Scothbond Multipurpose). The samples were sectioned into three 1-mm-thick sections, which were differentiated by the root level (cervical, middle and apical) and tested for push-out BS. Assessment of failure mode was made under a stereomicroscope. Data were analyzed using repeated measures three-way ANOVA and Tukey's test. The root canal cross-section had a significant influence on BS (p<0.001), with the lowest values being observed in oval-shaped canals. The post technique also significantly affected the BS (p=0.018), with the resin-relined GFPs providing the highest BS values in both oval and circular-shaped canals. Irrespective of the cross-section of the root canal and post technique, there was no significant difference in BS in the cervical, middle and apical third of the root canal (p=0.084). In oval-shaped canals, the BS to intraradicular dentin at cervical, middle or apical level could be increased when the GFPs posts were relined.

Resumo O objetivo deste estudo foi comparar a resistência de união (RU) de pinos de fibra de vidro (PFV), cimentados a condutos com secção transversal ovalada ou circular reabilitados com diferentes técnicas de restauração com PFVs, em função do nível intrarradicular. Noventa raízes de pré-molares inferiores humanos, com 16 mm de altura, classificadas como possuindo canais ovais ou circulares, foram tratadas endodonticamente e preparadas para serem reabilitadas com uma das três técnicas de restauração com PFVs (n=15): 1) PFV único, 2) PFV reembasado com resina composta, e 3) PFV principal associado a pinos acessórios. Os PFVs foram cimentados com um agente resinoso de polimerização dupla (RelyX ARC), após o canal ter sido tratado com um sistema adesivo de condicionamento total de três passos (Adper Scothbond Multiuso). As amostras foram seccionadas em três fatias de 1 mm de espessura, de acordo com o nível da raiz (cervical, médio e apical)e foram submetidas ao teste de RU por push-out. A análise do modo de falha foi realizada com auxílio de um estereomicroscópio. Os dados foram analisados utilizando-se a ANOVA a três critérios para medidas repetidas e o teste de Tukey. A secção do conduto apresentou influência na RU (p<0,001), com os menores valores sendo observados nos condutos ovalados. A técnica de restauração com PFVs afetou significativamente a RU (p=0,018), tendo o PFV reembasado proporcionado os maiores valores de RU, tanto em condutos ovais quanto circulares. Independentemente da secção transversal do conduto radicular e da técnica de restauração com PFV, não houve diferença significativa na RU nos terços cervical, médio e apical (p=0,084). Nos canais de secção transversal ovalada, a RU à dentina intrarradicular nos níveis cervical, médio ou apical aumentou com o emprego de PFVs reembasados.

Evaluation of bond strenght between leucite-based and lithium disilicate-based ceramics to dentin after cementation with conventional and self-adhesive resin agents

The aim of this study was to compare the microtensile bondstrength of two heat-pressed ceramics (leucite-based - IPSEmpress Esthetic/ Ivoclar Vivadent, and lithium disilicate-based- IPS e.max Press/ Ivoclar Vivadent) to dentin with the use ofconventional and self-adhesive resin cements. The occlusal surfaceof 60 intact human molars was removed and the dentin wasexposed. Ceramic blocks were cemented randomly with regardto the cementation systems (n=10): conventional dual resincement (Variolink II/ Ivoclar Vivadent), conventional self-polymerizingresin cement (Multilink/ Ivoclar Vivadent), and dualself-adhesive resin cement (RelyX U100/ 3M ESPE). The dualcementation systems were photoactivated with a LED lightdevice (Radii Cal, SDI) for 40 seconds. The specimens were sectionedto obtain sticks of approximately 1 mm2 for microtensiletests on a universal testing machine (EMIC). The type of fracturewas analyzed under a scanning electron microscope. TheAnalysis of Variance (ANOVA) and the Tukey test (α=0.05)showed that there was no difference between types of ceramic.Average microtensile bond strength was higher for the conventionaldual resin cement (Variolink II) and the self-adhesive dualresin cement (RelyX U100), despite greater prevalence of prematureloss of the sticks with the latter. Average bond strengthwas lower when the conventional self-polymerizing resin cement(Multilink) was used. Leucite-based and lithium disilicate-basedcements present similar bond strength to the dentin withconventional dual resin cement (Variolink II) and a dual selfadhesivecement (RelyX U100)...

O objetivo deste estudo foi avaliar a resistência de união pormicrotração à dentina humana entre cerâmicas prensadas (abase de leucita - IPS Empress Esthetic/ Ivoclar Vivadent, e abase de dissilicato de lítio - IPS e.max Press/ Ivoclar Vivadent)após cimentação com agentes resinosos e convencionais eautoadesivos. As superfícies oclusais de 60 molares humanoshígidos foram removidas e a dentina foi exposta. A cimentaçãodos blocos cerâmicos foi realizada de forma aleatória de acordocom os sistemas de cimentação (n=10): cimento resinosodual convencional (Variolink II/ Ivoclar Vivadent), cimentoresinoso autopolimerizável convencional (Multilink/ IvoclarVivadent) e cimento resinoso dual autoadesivo (RelyX U100/3M ESPE). Os sistemas de cimentação duais foram fotoativadoscom aparelho de luz LED (Radii Cal, SDI) por 40segundos. Os espécimes foram seccionados para a obtençãode palitos com aproximadamente 1 mm2 para a realização doteste de microtração em máquina universal de ensaios (EMIC).O padrão de fratura foi analisado em microscópio eletrônicode varredura. A Análise de Variância (ANOVA) e o teste deTukey (α=0,05) mostraram que não houve diferenças entre ostipos de cerâmicas. Houve maiores médias de resistência deunião por microtração para o cimento resinoso dual convencional(Variolink II) e para cimento resinoso dual autoadesivo(RelyX U100), apesar de maior prevalência de perdas prematurasdos palitos com este cimento. Houve menores médias deresistência de união ao se utilizar o cimento resinoso autopolimerizávelconvencional (Multilink). As cerâmicas a base deleucita (IPS Empress Esthetic) e a base de dissilicato de lítio(IPS e.max Press) apresentaram resistência de união semelhanteà dentina ao se utilizar o cimento resinoso dualconvencional (Variolink II) e o dual autoadesivo (RelyX U100)...